dc.contributor.authorMemon, S.
dc.contributor.authorPaidar, M.
dc.contributor.authorOjo, O.O.
dc.contributor.authorCooke, Kavian O.
dc.contributor.authorBabaei, B.
dc.contributor.authorMasoumnezhad, M.
dc.date.accessioned2020-11-25T14:35:53Z
dc.date.accessioned2020-12-04T15:29:53Z
dc.date.available2020-11-25T14:35:53Z
dc.date.available2020-12-04T15:29:53Z
dc.date.issued2020-12
dc.identifier.citationMemon S, Paidar M, Ojo OO et al (2020) The role of stirring time on the metallurgical and mechanical properties during modified friction stir clinching of AA6061-T6 and AA7075-T6 sheets. Results in Physics. 19: 103364.en_US
dc.identifier.urihttp://hdl.handle.net/10454/18195
dc.descriptionYesen_US
dc.description.abstractIn this study, the modified friction stir clinching process was successfully utilized to weld the AA7075-T6 to AA6061-T6 aluminum alloys. The approach of this study was to appraise the influence of the stirring time (6, 12, and 18 s) on the metallurgical and mechanical behavior of the welded samples. The microstructural study demonstrated that stirring time significantly affected joint properties and material flow, which can be ascribed to the discrepancy in the properties of the Al alloys used in this study. Void, local melting and defect-free joints were produced under the stirring times of 6 s, 18 s, and 12 s respectively. It was found that tensile/shear strength increased significantly from 63.5 MPa to 109 MPa as the stirring time increased from 6 s to 12 s, while a further increase in the stirring time to 18 s significantly decreased the joint's strength to 76.1 MPa. The observed failed samples showed that stirring time did not influence fracture mode.en_US
dc.language.isoenen_US
dc.relation.isreferencedbyhttps://doi.org/10.1016/j.rinp.2020.103364en_US
dc.rights(c) 2020 Elsevier. This is an Open Access article distributed under the Creative Commons CC-BY-NC-ND licence (https://creativecommons.org/licenses/by-nc-nd/4.0/)en_US
dc.subjectModified friction stir clinchingen_US
dc.subjectAA7075-T6 aluminum alloyen_US
dc.subjectAA6061-T6 aluminum alloyen_US
dc.subjectStirring timeen_US
dc.subjectMode fractureen_US
dc.subjectMechanical propertiesen_US
dc.titleThe role of stirring time on the metallurgical and mechanical properties during modified friction stir clinching of AA6061-T6 and AA7075-T6 sheetsen_US
dc.status.refereedYesen_US
dc.date.Accepted2020-08-25
dc.date.application2020-09-24
dc.typeArticleen_US
dc.type.versionPublished versionen_US
dc.date.updated2020-11-25T14:36:18Z
refterms.dateFOA2020-12-04T15:30:23Z


Item file(s)

Thumbnail
Name:
1-s2.0-S2211379720318313-main( ...
Size:
15.60Mb
Format:
PDF
Description:
memon_et_al_2020