Bond between glass fibre reinforced polymer bars and high - strength concrete

Abstract

In this study, bond properties of glass fibre reinforced polymer (GFRP) bars embedded in high-strength concrete (HSC) were experimentally investigated using a pull-out test. The experimental program consisted of testing 84 pull-out specimens prepared according to ACI 440.3R-12 standard. The testing of the specimens was carried out considering bar diameter (9.5, 12.7 and 15.9 mm), embedment length (2.5, 5, 7.5 and 10 times bar diameter) and surface configuration (helical wrapping with slight sand coating (HW-SC) and sand coating (SC)) as the main parameters. Twelve pull-out specimens reinforced with 16 mm steel bar were also tested for comparison purposes. Most of the specimens failed by a pull-out mode. Visual inspection of the tested specimens reinforced with GFRP (HW-SC) bars showed that the pull-out failure was due to the damage of outer bar surface, whilst the detachment of the sand coating was responsible for the bond failure of GFRP (SC) reinforced specimens. The bond stress – slip behaviour of GFRP (HW-SC) bars is different from that of GFRP (SC) bars and it was also found that GFRP (SC) bars gave a better bond performance than GFRP (HW-SC) bars. It was observed that the reduction rate of bond strength of both GFRP types with increasing the bar diameter and the embedment length was reduced in the case of high-strength concrete. Bond strength predictions obtained from ACI-440.1R, CSAeS806, CSA-S6 and JSCE design codes were compared with the experimental results. Overall, all design guidelines were conservative in predicting bond strength of both GFRP bars in HSC and ACI predictions were closer to the tested results than other codes.