Microstructure development during low-current resistance spot welding of aluminum to magnesium
View/ Open
Main article (2.927Mb)
Download
Publication date
2019-06-14Rights
© 2019 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution (CC BY) license (http://creativecommons.org/licenses/by/4.0/).Peer-Reviewed
Yes
Metadata
Show full item recordAbstract
Resistance spot welding of aluminum (Al5754) to magnesium (AZ31B) alloys results in the formation of a variety of solidification microstructures and intermetallic compounds that may affect the in-service performance of the weld. This study evaluates the relationship between the welding parameters and the properties of the weld nugget that is formed, and clarifies the morphological and microstructural evolutions within the weld regions during the low-current “small-scale” resistance spot welding of Al5754 to AZ31B. The investigations included a combination of microstructural characterization and thermodynamic analysis of the weld region. The results show that the welding time and clamping force parameters have significant effects on the properties of the nugget formed. The optimal welding parameters were found to be 300 ms welding time and 800 N clamping force. Weld nuggets formed with lower welding time and clamping force were undersized and contained extensive porosity. Meanwhile, a clamping force above 800 N caused gross deformation of the test samples and the expulsion of the molten metal during the welding process. The most significant microstructural changes occurred at the weld/base metal interfaces due to the formation of Al17Mg12 and MgAl2O4 intermetallic compounds as well as significant compositional variation across the weld pool. The thermal gradient across the weld pool facilitated the formation of several microstructural transitions between equiaxed and columnar dendrites.Version
Published versionCitation
Cooke KO and Khan TI (2019) Microstructure development during low-current resistance spot welding of aluminum to magnesium. Journal of Manufacturing and Materials Processing. 3(2): 46.Link to Version of Record
https://doi.org/10.3390/jmmp3020046Type
Articleae974a485f413a2113503eed53cd6c53
https://doi.org/10.3390/jmmp3020046