Loading...
Exploring the flowability, physical, and mechanical properties of eco-friendly colored cement mortars with metakaolin under sulfuric (H2SO4) and nitric acid (HNO3) attacks
Akbulut, Z.F. Guler, S. Osmanoglu, F. Kivanc, M.R.
Akbulut, Z.F.
Guler, S.
Osmanoglu, F.
Kivanc, M.R.
Publication Date
2024-08-15
End of Embargo
Supervisor
Rights
© 2024 Elsevier. Reproduced in accordance with the publisher's self-archiving policy. This manuscript version is made available under the CC-BY-NC-ND 4.0 license.
Peer-Reviewed
Yes
Open Access status
openAccess
Accepted for publication
2024-04-26
Institution
Department
Awarded
Embargo end date
Additional title
Abstract
This article aims to investigate the flowability, physical, mechanical, and durability properties of metakaolin (MK)-added colored cement mortars exposed to the effects of H2SO4 sulfuric acid (SA) and HNO3 nitric acid (NA). MK was used in 20% replacement with cement, and yellow (YP) and red pigments (RP) were added to the mixtures at 1% and 3% of the cement by weight. According to the results, although MK reduced the workability and, therefore, the flow diameter (FD) of mortars, thanks to the void-filling feature of MK, filling the voids in the microstructure caused the samples' apparent porosity (AP) and relative dynamic modulus of elasticity (RDME) to decrease. Additionally, MK significantly improved the residual compressive (RCS) and residual flexural strengths (RFS) of the samples thanks to the calcium-silicate-hydrate (C-S-H) bonds it formed in the interior structure, owing to its high pozzolanic efficiency. Moreover, this improvement of MK is more remarkable in samples that remain subject to SA and NA attacks for more time.
Furthermore, while YP reduces the workability of mortars and, therefore, the FD value due to its needle-tipped grain structure, RP increases the FD value of the mortars with its spherical grain structure. However, YP and RP contributed to reducing the AP of the samples and increasing RCS and RFS capacities at a meager rate by showing a micro-filling effect. In addition, there were significant increases in the total color changes (E) of YP and RP-added colored mortar samples, especially after longer SA and NA attacks.
Version
Accepted manuscript
Citation
Akbulut ZF, Guler S, Osmanoglu F et al (2024) Exploring the flowability, physical, and mechanical properties of eco-friendly colored cement mortars with metakaolin under sulfuric (H2SO4) and nitric acid (HNO3) attacks. Journal of Building Engineering. 91: 109463.
Link to publisher’s version
Link to published version
Link to Version of Record
Type
Article